Resin Parameters
| UV wavelength | 365-405nm | Elongation at break | 70-80% |
| Density | 1.05-1.25g/cm³ | Molding shrinkage | 5.1-6.2% |
| Viscosity | 500-900 cP·mPa·s | Flexural strength | 15-25 MPa |
| Hardness | 71-75D | Flexural modulus | 350-800 MPa |
| Bottom exposure time | 20-40s | Normal exposure time | 1.5-3s |
| Heat deflection temp | 50-55℃ | Resin wash | Alcohol |
| Tensile strength | 20-28 MPg | Conservation period | 1.5 year |
Model Print
Recommended Printing Parameters
| Printer Model | Layer Thickness | Exposure Time | Light-Off Time | Bottom Exposure Time | Bottom Layer | Anti-Aliasing Level | Z Lift Distance | Z Lift Speed | Z Retract Speed |
| Photon Mono M7 Pro | 0.05mm | 2s | 2s | 25s | 4 | 1 | 8mm | 6mm/s | 6mm/s |
| Photon Mono M5s Pro (Normal printing mode) | 0.05mm | 3.6s | 1s | 30s | 5 | 1 | 8mm | 6mm/s | 6mm/s |
| Photon Mono M5s Pro (Fast printing mode) | 0.1mm | 3.8s | 1s | 30s | 5 | 1 | 5mm | 20mm/s | 20mm/s |
| Photon Mono M5s (Normal printing mode) | 0.05mm | 2.8s | 1s | 25s | 5 | 1 | 8mm | 5mm/s | 6mm/s |
| Photon Mono M5s (Fast printing mode) | 0.1mm | 3s | 1s | 25s | 6 | 1 | 5mm | 20mm/s | 20mm/s |
| Photon Mono M5 | 0.05mm | 2.8s | 1s | 25s | 5 | 1 | 8mm | 5mm/s | 6mm/s |
| Photon M3 Max | 0.05mm | 3s | 2s | 35s | 6 | 1 | 10mm | 2mm/s | 3mm/s |
| Photon Mono X 6Ks | 0.05mm | 2.5s | 0.5s | 20s | 5 | 1 | 8mm | 3mm/s | 4mm/s |
| Photon Mono X2 | 0.05mm | 2.5s | 1s | 20s | 5 | 1 | 8mm | 2mm/s | 3mm/s |
| Photon Mono 2 | 0.05mm | 2.5s | 1s | 25s | 5 | 1 | 6mm | 4mm/s | 6mm/s |
| Photon D2 | 0.05mm | 2.5s | 1s | 28s | 5 | 16 | 5mm | 2mm/s | 3mm/s |
| Photon M3 Plus | 0.05mm | 1.5s | 1s | 25s | 6 | 1 | 6mm | 6mm/s | 6mm/s |
| Photon M3 | 0.05mm | 2s | 1s | 25s | 5 | 1 | 6mm | 3mm/s | 4mm/s |
| Photon M3 Premium | 0.05mm | 2.5s | 1s | 25s | 2 | 1 | 8mm | 6mm/s | 6mm/s |
| Photon Ultra | 0.05mm | 2s | 1s | 35s | 5 | 4 | 5mm | 2mm/s | 2mm/s |
| Photon Mono X | 0.05mm | 2s | 1s | 28s | 4 | 1 | 8mm | 2mm/s | 3mm/s |
| Photon Mono 4K | 0.05mm | 2s | 1s | 40s | 6 | 1 | 6mm | 4mm/s | 6mm/s |
| Photon Mono X 6K | 0.05mm | 2s | 1s | 28s | 6 | 1 | 8mm | 2mm/s | 3mm/s |
| Photon Mono SQ | / | / | / | / | / | / | / | / | / |
| Photon Mono SE | / | / | / | / | / | / | / | / | / |
| Photon Mono | 0.05mm | 2.5s | 1s | 40s | 6 | 1 | 6mm | 4mm/s | 6mm/s |
| Photon S | / | / | / | / | / | / | / | / | / |
Color Type
Instructions for Use
(1) Before use:
Shake the liquid resin before use;
Clean the resin tank and the molding platform to keep the bottom of the resin tank in light
transmission.
(2) When using:
Unscrew the cap and add it to the resin tank according to the equipment requirements;
Select the correct print parameters and settings for printing.
(3) After use:
After printing, please use the matching tools for post-processing, including blade, diagonal
pliers,tweezers,containers,gloves;
ethanol(≥95%),lactate or isopropyl alcohol cleaning solution;
(4) Post-processing steps:
A. Remove the printed model from the molding platform with a blade;
B. Submerge the model in the cleaning solution, rinsed or ultrasonically washed, then taken
out and drained; ANYCUBlC Wash and Cure machines are suggested to ensure better effect.
C.Proper processing, such as removing support, polishing, coloring, etc.
Precautions
- The ideal condition for storing uncured resin is a cool, dark place at room temperature and protect from light
to avoid high temperature or sunlight.
- Suggested operating temperature is 18-35'c, and a low temperature may affect the printing effect, thus, the
resin can be properly preheated before use (not more than 60°C). - If the resin pigment settles, it can be used after stirring or shaking.
- In order to ensure the performance of the resin, please take out the model in time after cleaning to avoid the model soaking in water for a long time.
- To ensure the mechanical properties of the model, please perform post-curing in time after cleaning and drying.
- To ensure the ideal performance of the curable material, it is necessary to control the intensity and time of the
light source after curing.Therefore, the following steps are recommended:
(1) The intensity of mercury lamp or LeD light source is 5-10mW/m?, and the duration is no more than 1 hour (self-regulation);
(2)The exposure time in the sun (summer) is around 1 hour;
(3) Proximity or long-term exposure under strong light sources such as high-power high-pressure mercury
lamps is prohibited.
(4) lt is recommended to print in a dark room or be covered with a lid while printing as resin is a photosensitive
material.